Evidence of substrate roughness surface induced magnetic anisotropy in Ni80Fe20 flexible thin films

Beluskya, M, Lepadatu, Serban orcid iconORCID: 0000-0001-6221-9727, Naylorc, J and Vopsona, MM (2019) Evidence of substrate roughness surface induced magnetic anisotropy in Ni80Fe20 flexible thin films. Journal of Magnetism and Magnetic Materials, 478 . pp. 77-83. ISSN 0304-8853

[thumbnail of Author Accepted Manuscript]
Preview
PDF (Author Accepted Manuscript) - Accepted Version
Available under License Creative Commons Attribution Non-commercial No Derivatives.

7MB

Official URL: https://doi.org/10.1016/j.jmmm.2019.01.097

Abstract

Experimental and computational evidence of a surface roughness induced magnetic anisotropy in NiFe thin films coated onto substrates of various surface roughnesses is reported. Magnetic coercive fields of 15 nm NiFe thin films coated on substrates with approximately 7 nm average roughness were remarkably 233% larger than identical thin films coated onto smooth substrates with < 1 nm average roughness. The NiFe films coated onto rough substrates developed hard and easy axes, normally non-existent in NiFe Permalloy. A linear correlation of the incline angles of the hard axis hysteresis loops to the average roughness values of the individual substrates was observed, with 99% correlation level. Using a modified micromagnetics theory that incorporates the effects of surface roughness, it is shown the observed magnetic anisotropy arises due to the spatial anisotropy of the surface roughness, resulting in an effective in-plane uniaxial magnetic anisotropy with energy density up to 15 kJ/m3.


Repository Staff Only: item control page